Alloy/
UNS |
DESCRIPTION |
C
MAX |
Ni |
Cr |
OTHER |
AMS |
ASTM |
301 S30100 |
Chromium
nickel steel capable of attaining high
tensile strength and ductility by moderate
or severe cold working. |
.15 |
6.0-
8.0 |
16.0-
18.0 |
Mn 2.0MAX
S .03MAX
P .045MAX
Si 1.0MAX |
5517
5519
5518 |
A-167
A-177 |
302 S30200 |
General
purpose chromium nickel stainless steel.
Its corrosion resistance is superior
to that of Type 301.It can be cold worked
to high tensile strengths but withSlightly
lower ductility than Type 301. |
.15 |
8.0-
10.0 |
17.0-
19.0 |
Mn 2.0MAX
S .03MAX
P .045MAX
Si 1.0MAX |
5516 |
A-167 |
304 S30400 |
Low carbon
chromium nickel stainless and heat resistingSteel
somewhat superior to Type 302 in corrosion
resistance. |
.08 |
8.0-
10.5 |
18.0-
20.0 |
Mn 2.0MAX
S .03MAX
P .045MAX
Si 1.0MAX
|
5513 |
A-167 |
304L S30403 |
Very low
carbon chromium nickel steel with generalcorrosion
resistance similar to Type 304 but with
superior resistance to intergranular
corrosion following weldingor stress
relieving.It is recommended for use
in parts which are fabricated by welding
and which cannot be subsequently annealed.
|
.03 |
8.0-
12.0 |
18.0-
20.0 |
Mn 2.0MAX
S .03MAX
P .045MAX
Si 1.0MAX
|
5511 |
A-167 |
309 S30900 |
High corrosion-resistant,
chromium nickel grade with carbon limited
to .08 to reduce carbon precipitationduring
welding. |
.08 |
12.0-
15.0 |
22.0-
24.0 |
Mn 2.0MAX
S 1.0MAX
P .045MAX
Si .03MAX |
5523 |
A-167 |
310 S31000 |
Similar
to 309 with higher resistance to corrosion
and oxidation at elevated temperatures |
.25 |
19.0-
22.0 |
24.0-
26.0 |
Mn 2.0MAX
S .03MAX
P .045MAX
Si 1.5MAX |
5521 |
A-167 |
316 S31600 |
Chromium
nickel stainless and heat resisting
steel with Superior corrosion resistance
to other chromium nickel steels when
exposed to many types of chemical corrodents;
superior creep strength at elevated
temperatures. |
.08 |
10.0-
14.0 |
16.0-
18.0 |
Mn 2.0MAX
Si 1.0MAX
P .045MAX
Mo 2.0-3.0
S .03MAX |
5524 |
A-167 |
316L S31603 |
Low carbon
chromium nickel stainless steel with
general corrosion resistance similar
to Type 316 but with superior resistance
to intergranular corrosion following
welding or relieving. It is recommended
for use in parts which are fabricated
by welding and cannot be subsequently
annealed. |
.03 |
10.0-
14.0
|
16.0-
18.0 |
Mn 2.0MAX
Si 1.0MAX
P .045MAX Mo 2.0-3.0
S .03MAX |
5507 |
A-167 |
317L S31703 |
Similar
to 316L but with additional molybdenum
to improve corrosion resistance. |
.03 |
11.0-
15.0 |
18.0-
20.0 |
Mn 2.0MAX
Si 1.0MAX
P .045MAX
Mo 3.0-4.0
S .03MAX |
|
A-167 |
321 S32100 |
Chromium
nickel steel containing titanium. Recommended
for parts fabricated by welding which
cannot be subsequently annealed. Also
recommended for parts to be used at
temperatures Between 800°F; and 1850°F. |
.08 |
9.0-
12.0 |
17.0-
19.0 |
Mn 2.0MAX
S .03MAX
P .045MAX
Si 1.0MAX
Ti 5xC MIN |
5510 |
A-167 |
347 S34700 |
Chromium
nickel steel containing columbium and
tantalum which is recommended for parts
fabricated by welding which cannot be
subsequently annealed. Also recommended
for parts to be used at temperatures
between 800°F; and 1850°F. |
.08 |
9.0-
13.0 |
17.0-
19.0 |
Mn 2.0MAX
S .03MAX
P .045MAX
Si 1.0MAX
Cb + Ta
10xC MIN |
5512 |
A-167 |
CARPENTER
20
CB33, 10
N08020 |
A highly
corrosion-resistant alloy used in the
chemical industry for applications where
corrosion resistance is extremely critical,
superior to the general run of 300 type
stainless. |
.06 |
32.5-
35.0 |
19.0-
21.0 |
Cu 3-4
8xC
Cb+Ta 1
Mo 2-3
Fe bal. |
|
B-463 |
430S 43000 |
General
purpose grade, corrosion-resistant,
straight chromium grade, non-heat-treatable. |
.12 |
|
16.0-
18.0
|
Mn 1.0MAX
S .03MAX
P .04MAX
Si 1.0MAX |
5503 |
A-176 |
446S 44600 |
Corrosion
and heat resisting chromium steel with
the maximum amount of chromium. Used
principally for the manufacture of parts
capable of resisting destructive scaling
in temperatures up to 200°F. |
.20 |
|
23.0-
27.0 |
Mn 1.5MAX
Si 1.0MAX
P .04MAX
N .025MAX
S 0.3MAX |
|
A-176 |
410S 41000 |
General
purpose corrosion and heat resisting
chromium steel.Good corrosion resistance
and fair machining properties.Can be
treated to RC35/45. |
.15 |
|
11.5-
13.5 |
Mn 1.0MAX
S 1.0MAX
P .04MAX
Si 1.0MAX |
5504 |
|
420S 42000 |
Chromium
steel capable of hardening to a maximum
of approximately RC53/58. |
.15
min. |
|
12.0-
14.0 |
Mn 1.0MAX
S .03MAX
P .04MAX
Si 1.0MAX |
5506 |
A-176 |
17-7PHTM4
S17700 |
A chromium
nickel stainless steel with characteristics
of good workability, easy hardening,
high strength,and excellent mechanical
properties at elevated temp., can be
heat treated at relatively low temperature
for high strength properties. |
.09 |
6.5-
7.75 |
16-
18.0 |
Al .75-1.5
S .03MAX
Si 1.0MAX
P .04MAX |
5528 |
A-693 |
17-4PHTM4
S17400 |
Precipitation
hardening stainless steel with high
strength and good corrosion resistance
to 600°F. Used in aerospace, chemical,
petrochemical, paper andmetalworking
industries. |
.07 |
3.0-
5.0 |
15.0-
17.5 |
Mn 1.0MAX
Si 1.0MAX
P .04MAX
Cu 3.0-5.0 |
5604 |
A-693
(Type
630) |
PH15-7MoTM4
S15700 |
Similar
to 17-7PHTM4 alloy, but with molybdenum
addedfor higher strength with heat treatment. |
.09 |
6.50-
7.75 |
14.0-
16.0 |
Mn 1.0MAX
S .04MAX
Si 1.0MAX
Mo 2.0-3.0
P .04MAX
Al .75-1.50 |
5520 |
A-693 |
A286TM4
S66286 |
An iron,
nickel, chromium alloy designed for
service up to 1300°F where high strength
and corrosion resistance are required. |
.08 |
24.0-
27.0 |
13.5-
16.0 |
Mn 2.0MAX
Ti 1.9-2.35
Si 1.0MAX
Mo 1.0-1.5
P .040MAX
V 0.10-0.50
Al .035
S .030MAX |
525 |
|
AM 350TM8
S35000 |
ar to
17-7PHTM4 alloy and PH15-7MoTM4 alloy,
but with slightly higher elevated temperature
capability. |
.07-
.11 |
4.0-
5.0 |
16.0-
17.0 |
Mn .50-1.25
S .03MAX
Si .50MAX
Mo 2.5-3.25
P .04MAX
N .07-.13 |
548 |
A-693 |